New type of high alumina brick lead smelting furnace in different parts of which use

Lead smelting of lead sulfide concentrate, usually contain a certain amount of Zn, in the smelting process is also the oxidation of ZnS, while part of the reduction, part of the re-oxidation into the lead-rich slag, part of the form of steam into the flue gas, With the flue gas rising again in the process of secondary air oxidation, or contact with other elements after oxidation, while the flue gas contains large amounts of SO2 gas and high oxygen partial pressure. In the melt contains a lot of PbO and metal Pb, along with other normal slag composition, that is, FeO, CaO, SiO2, Fe3O4 and other impurities.

Melt a large number of PbO and Pb are low melting point material, in the 1000-1150 ℃ melting temperature, have good mobility and penetration, it is easy to penetrate into the cracks within the refractory brick. Pb infiltration into the brick body gap, the oxygen is oxidized into PbO, the volume will increase about 20%, which will greatly fill the gap of high alumina brick.

In addition, during the use of high-alumina bricks, the melt penetrates into the high-alumina bricks along the capillary channels such as pores and cracks, and interacts with it to form a metamorphic layer different from the original Clay, High Alumina insulating bricks. When the furnace temperature Fluctuations, the metamorphic layer will crack, peeling, melt deeper into the brick, the thicker the metamorphic layer, the thicker peeling structure. If the local oxygen potential in the furnace is high, it is easy to reoxidize the Cr2O3 in the local high alumina brick, and Cr3 + is oxidized to cr6 +, so that PbO reacts with CrO3 due to the strong basicity, and low PbO · CrO3 is formed, Anti - scouring performance of Bottom Frame &Skid Platform Brick for Heating Furnace.

At the same time, and the formation of high alumina brick Cr2O3 and other substances are a lso low melting point material, is not conducive to the formation of high melting point solid phase material. ZN vapor in the flue gas, if combined with Fe2O3 in the high-alumina refractory brick for sale, is reduced to a low-melting FeO phase and Zn is oxidized to ZnO, the volume of ZnO will be expanded by 5-6 times, In the infiltration of parts of the expansion effect. SO2 components within the flue gas, etc. on the composition of high alumina brick also has a certain chemical effect.

The characteristics of these slag and flue gas characteristics of high-alumina smelting furnace metallurgical furnace use has special requirements.

2016年12月20日星期二

Bottom Frame &Skid Platform Brick for Heating Furnace---Refractory Brick---Refractory Material---Changxing Refractory

Bottom Frame &Skid Platform Brick for Heating Furnace

Introduction, Advantages, Application:

Skid and platform brick are with brown corundum and high grade bauxite as raw materials, using low cement technology and additive. Casting moulding and baking at low temperature, or casting on-site are both available. Characterized by high strength, water and corrosion resistance, they are used for isothermal bed and furnace doorframe of continuous heating furnace and have good effect.

Content source:
http://www.yilongrefractory.com/AllProductOneServlet?id1=1&id=10
E-mail:sales8@chinaelong.com

2016年12月19日星期一

Tundish Well Block---Refractory Brick---Refractory Material---Changxing Refractory

Tundish Well Block

Introduction:
Changxing Refractory supplies refractory nozzles in a number of different compositions to best suit the operating conditions of steel ladle. Nozzles are available in alumina qualities (with and without carbon additions, zirconia additions, and/or chrome additions) to best resist the slag chemistry. Nozzles are either pressed or pre-cast depending on the composition.

Advantages:
1. These shapes can be pre-fired if necessary to ensure optimum performance.
2. These pieces are custom designed for a specific ladle with attention to total life, free open performance and cost.

Application:
1. Suitable for well block of tundish nozzle under different process conditions
2. Can be assort with billet nozzle. changer, common metering nozzle stopper for slab and slide plate

Content source:
http://www.yilongrefractory.com/AllProductOneServlet?id1=1&id=9
E-mail:sales8@chinaelong.com

2016年12月15日星期四

Ladle Permeable Well Block---Refractory Brick---Refractory Material---Changxing Refractory

Ladle Permeable Well Block

Introduction:
Made from high-purity, high-density, high-strength materials and MAS matrix-optimized system, shaped by pressing, prefabrication and vibration. With subtle formula design, unique technical process, they have, which identified up to the leading domestic level and received recognition and praise.

Advantages:
1. Good corrosion/erosion resistance 2. High temperature performance 3. Longer service life 4. Stable structure 5. Thermal shock resistance

Application:
They suit specially for large-sized refining ladles

Content source:
http://www.yilongrefractory.com/AllProductOneServlet?id1=1&id=8
E-mail:sales8@chinaelong.com

Ladle Permeable Brick---Refractory Brick---Refractory Material---Changxing Refractory

Ladle Permeable Brick

Ladle Permeable Brick---Refractory Brick---Refractory Material---Changxing Refractory
Ladle permeable is also called ladle purge plug or brick. Adopting tabular alumina, emery, chromium oxide green and magnesia alumina spinel as main raw materials, using cement as binder. Ladle purge plug is used for ladle bottom blowing.
Introduction:
Ladle permeable is also called ladle purge plug or brick. Adopting tabular alumina, emery, chromium oxide green and magnesia alumina spinel as main raw materials,using cement as binder. Numerous designs are available based around high purity refractory materials. They can be designed and produced types of straight hole, directional slit, directional labyrinth, girth shape and interior and exterior integral split etc according to users requirement. With precisely formed slot/channel for the optimum gas flow rates and stirring efficiency

Advantages:
1. Stable structure 2. Consistent quality 3. Strong corrosion resistance 4. Long service life 5. High air permeability 6. Reliable gas flow performance

Application:
Ladle purge plug is used for ladle bottom blowing.

Content source:
http://www.yilongrefractory.com/AllProductOneServlet?id1=1&id=7
E-mail:sales8@chinaelong.com

2016年12月14日星期三

Refractory brick and clay fire brick distinction

refractory brick and fireclay refractories distinction
Clay refractory bricks are a kind of refractory bricks, the precise definition of refractory products are shaped, from the delivery form of distinction is a series of refractories.

Refractories are divided into ordinary refractories (1580 ~ 1770 ℃), advanced refractories (1770 ~ 2000 ℃) and special refractories (2000 ℃ above); according to the chemical characteristics of acid refractories, Neutral refractories and refractories. In addition, there are special occasions for the refractory material.

Now the definition of refractory, has not only depends on whether the refractoriness of 1580 ℃ or more. refractory brick for sale refers to the current application of metallurgical, petrochemical, cement, ceramics and other production equipment lining the inorganic non-metallic materials.

Acid refractories to silicon oxide (SiO2) as the main component, commonly used silica brick and clay brick. Silica brick is more than 93% SiO2 silica products, the use of raw materials are silica, waste silica brick. Silica brick acid-resistant slag erosion ability, but susceptible to the erosion of slag, and its load softening temperature is high, close to its refractoriness, after repeated calcination volume does not shrink, or even a slight expansion, but the thermal shock resistance is poor. Silica brick is mainly used for coke oven, glass furnace, acid furnace and other thermal equipment, silica brick in accordance with the SiO2 content and physical and chemical indicators can be divided into several levels, mainly divided into glass kiln silica brick and coke oven silicon Brick two categories. Clay brick or refractory clay clinker as the main raw material, containing 30% to 46% of alumina, refractoriness 1580 ~ 1770 ℃, is a weak acid refractory, good thermal shock resistance, acid slag corrosion resistance , Widely used in clay bricks to refractory clay as the main raw material is called ordinary clay bricks to coke gem clinker as the main raw material made of porosity was 17% below the clay brick known as low porosity clay brick. Two kinds of clay brick and according to which the physical and chemical indicators are divided into several grades, ordinary clay brick and low porosity clay brick between the price difference.

Neutral refractories to alumina, chromium oxide, silicon carbide or carbon as the main component. Neutral Refractory company in the main products are: corundum bricks, high alumina bricks, silicon Mo brick, mullite bricks, aluminum chrome bricks, aluminum carbon brick, graphite or carbon brick. High alumina products in the main crystalline phase is mullite and corundum, corundum content increases with increasing alumina content, alumina containing 95% of the corundum products is a wide range of high-quality refractory material containing alumina 95% of the corundum products is a wider use of high-quality refractories. The chrome brick with chromium oxide as the main component has good corrosion resistance to steel slag, but the thermal shock resistance is poor and the softening degree is low. High alumina bricks of the indicators are relatively good, with good cost-effective, so widely used, but because of high alumina brick erosion resistance is poor, it can not be applied to the key conditions of complex conditions, silicon brick is the use of aluminum Bauxite and silicon carbide as the main raw materials, mainly used in the transition zone of cement rotary kiln.

Carbon refractories are carbon brick, graphite products and silicon carbide products. Carbon products is another kind of neutral refractory material, which is divided into three categories: carbon brick, graphite product and silicon carbide based on the composition of carbonaceous material and the mineral composition of products. Carbon brick is a high-grade petroleum coke as raw material, plus tar, asphalt binder, at 1300 ℃ isolated from the firing of air conditions. Graphite products (except natural graphite) with carbonaceous materials in the electric furnace in 2500 ~ 2800 ° C in the graphite system in the system. Silicon carbide products are silicon carbide as raw materials, plus clay, silica and other binder in 1350 ~ 1400 ℃ firing. Silicon carbide plus silicon powder can also be made in the electric furnace nitrogen atmosphere under silicon nitride - silicon carbide products. Carbon products, low thermal expansion coefficient, high thermal conductivity, good thermal shock resistance, high temperature strength. Long-term use at high temperatures do not soften, from any acid erosion, a good salt resistance, not by the metal and slag wetting, light weight, high-quality high-temperature materials. Disadvantage is easily oxidized at high temperatures, should not be used in the oxidizing atmosphere. Carbon products are widely used in high-temperature furnace lining (bottom, hearth, lower furnace, etc.), melting non-ferrous metal furnace lining. Graphite products can do the reaction tank and petrochemical autoclave lining. Silicon carbide and graphite products can also be made of melting copper alloy and light alloy crucible. Carbon brick and graphite products, the main component of carbon (C), the thermal expansion coefficient is very low, high thermal conductivity, good thermal shock resistance, high temperature strength, acid and salt erosion, especially weak acid has good resistance , Free from metal and slag wetting, light, generally used in iron and steel smelting industry, but also for petroleum, chemical industry, autoclave lining. Silicon carbide is an excellent refractory, good corrosion resistance, but at high temperatures (more than 1400 degrees) is easy to oxidize, not suitable for use in the oxidizing atmosphere.

The main refractory products are magnesia and oxygen. The main products include magnesia brick, magnesia-chrome brick, Spinel brick and so on. Magnesia (MgO) more than 80% of the fire brick called magnesium bricks, according to the index can be divided into many grades of grades, magnesium bricks on the slag and iron slag has a good resistance, refractoriness than clay brick and silica brick high. Mainly used for open hearth, oxygen blowing converter, electric furnace, non-ferrous metal smelting equipment and glass industry and some high-temperature equipment. Magnesia-chrome brick on the resistance of the slag stronger, and the thermal shock stability is also much higher than the magnesium brick, so the application of more extensive, magnesia-chrome brick in the iron and steel smelting and non-ferrous metal smelting industry has almost replaced magnesium brick, Because of its chromium oxide (Cr2O3) can continue to spread, the magnesia-chrome brick can be easily linked to the kiln skin, so in the last 30 years, has been the first choice for cement kiln firing refractories, magnesia chrome brick Cr2O3 Will react with water, trivalent chromium can become hexavalent chromium, will cause pollution of water, is facing the trend of gradually withdraw from the cement industry market. Magnesia-alumina brick using magnesia and alumina as raw materials, compared with magnesia brick, its thermal shock stability and high temperature creep performance is better, use the site and almost the same as magnesium bricks. Dolomite brick and magnesium calcium brick performance is almost the same, dolomite brick to dolomite as raw materials, magnesium calcium bricks to synthetic magnesium calcium sand as raw materials, oxygen content is generally 15-30%, the remaining components are mainly magnesium oxide, with The role of purification of molten steel, generally only for the special steel smelting, magnesium calcium brick production process is more complex, easy to hydration and decomposition of water and steam, not easy to transport, the use of the process must be prepared to prevent work. Manganese iron spinel brick is a new product, mainly used for cement rotary kiln firing zone and transition zone, will be the cement industry alternative to magnesia chrome brick main products.

Refractory materials such as carbides, nitrides, borides, silicides and sulphides, such as alumina, lanthanum oxide, beryllium oxide, oxygen, zirconia and the like, are used in special applications. (Silicon carbide, titanium carbide, tantalum carbide, etc.), nitrides (boron nitride, silicon nitride and the like), borides (borides (borides), and the like); refractory materials having a melting point of 2050 to 3050C or higher; Zirconium, titanium boride, hafnium boride, etc.), silicides (such as molybdenum disilicide), and sulfides (thorium sulfide, cerium sulfide, etc.). Their melting point for the 2000 ~ 3887 ℃, of which the most refractory is the carbide. High temperature composites such as metal ceramics, high temperature inorganic coatings and fiber reinforced ceramics.

Special materials are often used AZS brick (ie, zirconia corundum brick), corundum brick, direct combination of magnesia-chrome brick, silicon carbide brick, silicon nitride bonded silicon carbide brick, nitride, silicide, sulfide, boride, carbonation And other non-oxide refractory materials; oxygen, chromium oxide, aluminum oxide, magnesium oxide, beryllium oxide, and other refractories. Commonly used insulation refractory products are diatomite, asbestos products, such as insulation boards. Refractory refractory materials are often used in refractory castables, refractory mud, refractory ramming material, refractory plastic, fill charge, refractory gunning materials, refractory materials, refractory coatings, lightweight refractory castable, gun mud and so on.

2016年12月13日星期二

Ladle Nozzle Well Block---Refractory Brick---Refractory Material---Changxing Refractory

Ladle Nozzle Well Block

Ladle Nozzle Well Block---Refractory Brick---Refractory Material---Changxing Refractory
The series of well blocks for nozzles are made from high-purity, high-density, high-strength materials. Based on different materials, they have corundum, magnesia carbon and alumina spinel carbon.It is mainly used to fix upper nozzle in steelmaking.
Introduction:
The series of well blocks for nozzles are made from high-purity, high-density, high-strength materials. Based on different materials, they have corundum, magnesia carbon and alumina spinel carbon.

Advantages:
They show the features of stable structure, excellent thermal shock resistance, good corrosion/erosion resistance and long service life.

Application:
It is mainly used to fix upper nozzle in steelmaking.

Content source:
http://www.yilongrefractory.com/AllProductOneServlet?id1=1&id=6
E-mail:sales8@chinaelong.com

2016年12月12日星期一

Low Carbon Brick and Carbon-free Brick---Refractory Brick---Refractory Material---Changxing Refractory

Low Carbon Brick and Carbon-free Brick

Low Carbon Brick and Carbon-free Brick---Refractory Brick---Refractory Material---Changxing Refractory
Low carbon magnesia carbon brick are used for ladle slag line. Low carbon and carbon-free corundum spinel bricks are used for ladle lining and bottom.It can realize ladle low carbon and carbon-free to meet the needs of high grade and ultra-clean steel. 
Introduction,Advantages and Application:

Low carbon magnesia carbon brick using with crystal magnesite, fused corundum, fused spinel, high purity and ultrafine graphite and nano composite antioxidant as raw materials, which are used for ladle slag line. Low carbon and carbon-free corundum spinel bricks are used for ladle lining and bottom. It can realize ladle low carbon and carbon-free to meet the needs of high grade and ultra-clean steel. The products are characterized by corrosion resistance, penetration resistance, erosion resistance, spalling resistance and good integrity, to meet the need of complete refining ladle. It is the leading level in the domestic.

Content source:
http://www.yilongrefractory.com/AllProductOneServlet?id1=1&id=5
E-mail:sales8@chinaelong.com

2016年12月8日星期四

Ladle Magnesia Carbon Brick---Refractory Brick---Refractory Material---Changxing Refractory

Ladle Magnesia Carbon Brick

Introduction:
Magnesia Alumina Carbon Brick is formulated for ladle linings and is manufactured with very high purity electro fused Magnesia, high purity Graphite, Alumina and Antioxidants

Advantages:
High purity Alumina and Magnesia thermal shock properties. It has the performance between magnesia carbon brick and alumina magnesia carbon brick

Application:
They are used in Ladle linings, ladle upper and lower slag line, ladle wall and ladle bottom

Content source:
http://www.yilongrefractory.com/AllProductOneServlet?id1=1&id=3
E-mail:sales8@chinaelong.com

2016年11月30日星期三

Advanced insulation material ceramic fiber blanket that used for industrial furnace

Advanced insulation material ceramic fiber blanket that used for industrial furnace
Advanced insulation material ceramic fiber blanket that used for industrial furnace
Ceramic fiber blanket, also known as aluminum silicate fiber blanket. Because one of the main components is alumina, and alumina is the main component of ceramic, so it is called ceramic fiber blanket. Ceramic fiber blanket is made by special aluminum silicate ceramic fiber filament with a special double-sided acupuncture process. Double-sided acupuncture process greatly improved the degree of fiber interwoven, tensile strength and surface roughness. Fiber blanket does not contain any organic binder, that is to make sure the ceramic fiber blanket have good stability at high temperature or low temperature.

Ceramic fiber blanket, with white color, regular size, does not contain any binding agent, and the refractory temperature is 950-1400 Degrees Celsius. It has low thermal conductivity, low heat capacity, excellent chemical stability, thermal shock resistance, tensile strength, and sound absorption. In neutral, oxidizing atmosphere, ceramic fiber blanket still could maintain good tensile strength, toughness and refractory fiber board structure after long-term use, is an excellent Insulating material.

Ceramic fiber blanket can be used in aerospace, steel, petrochemical high temperature insulation; military equipment fire insulation; industrial kiln, heating device wall lining insulation; high temperature equipment insulation; high temperature pipe insulation; electrical components thermal resistance; raw material of gasket; module, folding block.

Article source:
http://www.yilongrefractory.com/news/Advanced%20insulation%20material%20ceramic%20fiber%20blanket%20that%20used%20for%20industrial%20furnace.html
E-mail:sales8@chinaelong.com

2016年11月27日星期日

Fire - resistant fire shutter doors Fire - resistant insulation Fire cloth

Cement furnace rotary kiln insulation board; various types of heat treatment furnace fiber insulation; clay insulating bricks tunnel kiln flat ceiling construction; industrial furnace full-fiber insulation; castable high temperature plastic; light insulating refractory cement material; ceramic fiber module folding block; ceramic fiber shell, pouring Crossing and other special-shaped vacuum products;

Various types of 304,310 anchor; conventional and special-shaped module, folding block; lining design; fire; selection of technical guidance; lining material; rock wool; asbestos; glass fiber; slag cotton; . My company to undertake a variety of high-temperature equipment products

Custom, high insulating brick technical advisory guidance, construction and renovation projects.
Ceramic fiber cloth with rope Product Description: It is made of ceramic fiber yarn and silk yarn reinforcement (fiberglass or alloy steel wire) made of ceramic fiber cloth, belt, rope and other high temperature products. Products with high temperature resistance, good flexibility,insulation products  machinability, not only has a high temperature

Thermal insulation properties, both the flexibility of ordinary textiles.
Features: Excellent clay insulating bricks properties; excellent tensile properties; excellent high temperature strength; excellent electrical insulation properties; excellent acid, oil, water vapor corrosion; low thermal conductivity; non-toxic non-toxic asbestos , No adverse effects on the environment.
Typical applications: petrochemical industry, soft tube furnace tube; industrial furnace curtain, door seal; high temperature pipe, container insulating castable; cable or fuel pipeline protection; high temperature protection, composite materials; fire package, fire shutter doors.

2016年11月21日星期一

Characteristics and Application of Refractory Castables with High Aluminum and Low Cement Content

Low Cement Castable
Low cement castable can be widely used for those industrial furnace's working lining, permanent lining( working temperature under 1400c), such as little refining Ladle cover, Ladle & Tundish permanent layer, heating furnace working wall, top and bottom. Blast furnace body, Hot metal ladle permanent layer.
The traditional refractories castable is made of refractory aggregate and high alumina cement. During the preparation process, the particle gradation of the fine aggregate fraction was not well designed. Cement particles are also coarse (specific surface area is generally 3000cm2 / g or so), the amount of cement is generally 15 to 25 percent, and the construction water consumption is 10 to 15 percent. Coupled with the amount of cement and more coarse particles, so that the cement can not be fully hydrated, resulting in poor performance of castables.

Low cement castable refractory castable is to overcome the shortcomings of the traditional refractory castable, the use of lower cement content, ultrafine powder technology, the correct design of aggregates push collection, and the use of highly efficient surface-active additives and other comprehensive technical measures prepared from, With the traditional refractory material pouring

High solidification rate, good volume stability, after drying and calcination, the volume shrinkage is small "and so on. It has the characteristics of low cement content, high compactness and low porosity, high normal temperature curing strength, good volume stability.

"GJ-180 high-strength refractory company castable" is based on fused white fused alumina as aggregate with pure calcium aluminate cement as the binder made of. The highest temperature of use of this casting material to 1800 ℃, 1400 ℃ under the hot state of the flexural strength of 7.4MPa, at high temperatures also has a good Wear resistance. It is suitable for the new kiln dry kiln cement kiln, three-channel coal nozzle and other parts used.

"GJ-18S castable" is fused white corundum as aggregate, it is a low cement content of refractory castable, the castable has a high mechanical strength and erosion resistance, erosion resistance, the maximum temperature of 1600 ℃ , Depending on its performance, this castable is suitable 1000 ~ 1400 ℃, the impact of serious wear and tear of large cement kiln mouth, multi-cylinder cooler elbow and other parts used.

"LC-160 castable" is a low-cement refractory castable, is based on high alumina bauxite clinker aggregate, pure calcium aluminate cement as a binder prepared, suitable for small and medium-sized dry kiln cement kiln mouth, Cooler elbow parts apply.

"GJ-15B (or GJ-15A) castable" commonly known as alkali-resistant high-alumina low-cement refractory castable, refractory brick for sale, it is through the matrix composition of the adjustment and control of preparation, with high mechanical strength, alkali corrosion, Temperature of 1500 ° C, suitable for cement production

The original, the fuel contains alkali, sulfur, chlorine high number of large dry kiln.

Refractory Balls---Used for HBS Regenerator---Changxing Refractory material

Refractory Balls---Used for HBS Regenerator---Changxing Refractory material
Refractory Balls---Used for HBS Regenerator---Changxing Refractory material
Refractory Balls Used for HBS Regenerator

Application:
Application of regenerator in gas burning industrial furnace combustion system

Introduction and Advantages:
According to the structure of regenerator different, many kinds of products, good thermal shock resistance, large heat storage capacity, high strength, easy to clean, can be repeated use.

Content source:
http://www.yilongrefractory.com/ProductServletOne?id1=4&id=82
E-mail:sales8@chinaelong.com

2016年11月16日星期三

Precautions and repair measures of masonry refractory concrete precast block

Masonry refractories concrete prefabricated block must pay attention to the following matters:
1) refractory concrete prefabricated blocks of brick masonry joints for the 5mm ~ 10mm.
2) Masonry mud used should be consistent with the pre-block material.
3) masonry should be on the bottom surface of the prefabricated block on the surface of pulp, and then re-line. When hanging, should also be in the corresponding side of the pulp.
4) After the completion of each layer of prefabricated blocks, fill the joints in the refractory brick concrete.
5) cut off the ring, tie or fill in the vicinity of mud.
6) dome arch, the arch should try to tighten the sides.
7) masonry prefabricated block, such as the gap is too large, can be used in place of cast-in-place refractory castable concrete or fire brick plug.
silica ramming mass concrete repair methods:
  1) crack repair lining lining cracks, may not repair. But the emergence of thick cracks, cracks should be looking at the location, analysis of whether the impact on the lining life, can not form a large peeling. Where important parts, must be repaired.
Repair, first with water to wet. Usually in the thick stitch filled with homogeneous refractory material concrete, tapping formation. If the seam can be repaired into V-shaped re-repair, the effect is better. If a large slit appears in the lining, two slightly larger round holes can be cut at the two ends of the seam

, Re-block, so to prevent the spread of further expansion of the crack.
  2) peeling patching repair, should first clean up the peeling, sprinkle some water, and then the preparation of good homogeneous refractory concrete fill. Be careful when patching tightly wiping light. Repair to pay attention to the oven, the time is about 12h, then you can put into use.

Steel fiber reinforced low cement refractory castable

A heat-resistant steel fiber of a certain size is added to a castable refractories in a mixture consisting of a refractory material aggregate, a binder and an admixture to become

a steel fiber reinforced refractory castable. Compared with castables without heat-resistant steel fireclay refractories, the castable has the following characteristics:
1, can inhibit castable in the curing, baking and high temperature use in the contraction;
2, to improve the toughness of castable, anti-mechanical impact and mechanical strength;
3, to improve the thermal shock resistance of castable;
4, to prevent the cast material generated within the micro-cracks in the thermal stress and mechanical stress under the expansion or extension caused by the occurrence of fracture or peeling.

2016年11月14日星期一

Tundish Impact Plate----Changxing Refractory Material---used for steel plant

Tundish Impact Plate

Tundish Impact Plate----Changxing Refractory Material---used for steel plant
Tundish Impact Plate----Changxing Refractory Material---used for steel plant
Introduction:
An impact plate formed from a refractory material for reducing the turbulence of a molten metal poured therein. The impact pad has a plurality of sidewalls, each sidewall having a plurality of spherically shaped portions. The spherically shaped portions disperse the molten metal in a variety of directions.

Advantages:
They are characterized by good slag resistance, high hot strength and long service life. Such products can be rationally matched according to requirements by processing, service time and cleaness of molten steel.

Application:
good thermal shock resistance, high temperature resistance, good erosion resistance and long service time.

Contect  source:
http://www.yilongrefractory.com/ProductServletOne?id1=4&id=56
E-mail:sales8@chinaelong.com

2016年11月7日星期一

New requirements of second generation dry process cement for refractory

China's cement industry developed rapidly, the output from the early liberation of the development of 620,000 t in 2015 to 2.35 billion t, from 1985 onwards 31 consecutive years of production and consumption ranked first in the world, the new dry cement production technology and equipment level Has been close to the international advanced level, localization of equipment has been fully meet the needs of the cement industry. However, excess capacity of cement clinker in China, cement companies operating efficiency and low efficiency. Energy saving, reduce costs as a cement enterprise to enhance the economic benefits of the inevitable. China Building Materials Federation first proposed the cement industry should vigorously develop the "second-generation new dry cement technology", its purpose is to reduce the energy consumption of cement production and enhance business efficiency. refractory material as an indispensable lining process of cement sintering material, is the second generation of new dry process cement material support conditions. The second generation of new dry cement technology on the refractory materials put forward new requirements, and refractory configuration technology should also be compatible with.
Cement industry, the initial requirements of refractories materials to meet the protection of the metal shell of a single function; and the development of the second generation of new dry cement technology, requiring refractories with energy saving, green, longevity efficient, safe and stable and other functions .

Energy saving
The second generation of dry cement technology in the cement clinker heat consumption standards for the 650 cal  kg-1, and a large part of the calcination process of cement heat through the thermal radiation of the equipment surface dissipation. Therefore, the refractory company material as the basis of all high-temperature equipment lining material, should not only have good performance, but also should take into account the energy-saving insulation properties.
Green
The chromium content in the cement shall not be greater than 10.00 mg  kg-1. According to statistics, the water-soluble chromium (Ⅵ) in cement mainly comes from the fuel and raw materials of cement raw materials, crushing and grinding media, refractory materials (magnesia-chrome bricks) and chromium-containing wastes. For most cement companies, refractory high insulating brick (magnesia-chrome brick) is the most important source of water-soluble chromium (Ⅵ). Magnesia-chrome bricks because of good thermal shock resistance, high temperature resistance and hanging kiln skin capacity, is still the majority of domestic cement rotary kiln for the use of high-temperature zone. According to statistics, the domestic cement enterprises average per ton of cement clinker consumption of high-temperature zone with alkaline refractories of about 244 g, assuming that half of the bricks into soluble chromium (Ⅵ) and into the cement clinker, the cement clinker Soluble chromium (Ⅵ) content will reach 10.98mg  kg-1. Therefore, in the cement industry to eliminate the use of magnesia-chrome brick has been in the industry consensus, the major domestic basic refractories enterprises have developed alternative to magnesia-chrome brick refractory products used in high-quality, and in the country has been rapidly applied.
Longevity and high efficiency
New dry cement technology continues to move in the direction of large-scale development, the current Nissan 5000t and above cement clinker production line has become the minimum requirements of new projects of cement companies, Nissan 10000t or 1200t cement clinker production line in China has reached more than 10 articles. Large-scale cement production line requires the quality and stability of refractories alumina brick should be a corresponding substantial increase in long-life, high-performance refractories in the country to promote rapidly, the current domestic cement production line refractories have been slowly from the "overhaul a year "To" three years of two overhaul, "the goal of development.

Henan Xinmi Changxing Refractory Material Co., Ltd. Located in Henan Province,China.ChangXing's product portfolio covers shaped products such as refractory materials,refractory brick, refractory castable,refractory nozzle, ceramic fiber, slide gate, etc; unshaped products including repair, construction and casting mixes and mortars.exported to more than 20 countries, such as Thailand, Indonesia, Pakistan, Saudi Arabia, South Africa, Turkey, Iran, Iraq and so on.

Special - shaped refractory bricks of the insulation refractory bricks

With regular shape of the thermal insulation products. Belongs to the light insulation refractory material. The common characteristics of these materials is the small bulk density, light weight, low thermal conductivity. But the strength is low, high-temperature heavy burn contraction larger.
Specific type of firebrick high insulating brick Category:
Usually divided into three types: (1) ordinary insulation bricks, the use of temperature below 1000 ℃, mainly diatomaceous earth bricks, inflated razor stone bricks, expanded perlite bricks, thermal equipment for thermal insulation. (2) fire-resistant insulation bricks, the use of temperature between 1000-1500 ℃, mainly light clay bricks, light silica bricks, light aluminum bricks and so on. (3) high temperature Insulating Bricks, the use of temperature above 1500 ℃, and can be directly used as high-temperature furnace lining, mainly light corundum bricks, alumina hollow ball products and zirconia hollow ball products.
Ultra-high temperature insulation brick:
The ultra-high-temperature heat insulation bricks are made of at least one heat-resistant inorganic material such as silica, alumina, lithium oxide, magnesium oxide and viscose in the form of fibrous material such as silicon fiber, aluminum fiber, carbon fiber, nitrogen fiber and silicon carbide fiber Knot as raw materials, formed by sintering. This lightweight brick high strength, excellent heat resistance and thermal conductivity of ultra-high temperature, easy processing, suitable for spaceflight devices, industrial furnaces and so on.

Henan Xinmi Changxing Refractory Material Co., Ltd. Located in Henan Province,China.ChangXing's product portfolio covers shaped products such as refractory materials,refractory brick, refractory castable,refractory nozzle, ceramic fiber, slide gate, etc; unshaped products including repair, construction and casting mixes and mortars.exported to more than 20 countries, such as Thailand, Indonesia, Pakistan, Saudi Arabia, South Africa, Turkey, Iran, Iraq and so on.

2016年11月6日星期日

Refractory brick - --clay brick---Basic information


Properties of clay brick:
Clay brick is a weak acid refractory products, resistant to acidic slag and acid gas erosion, resistance to alkaline substances somewhat less. Clay refractory brick thermal performance is good, resistant to hot and cold.


The use of clay brick:
Clay, High Alumina Insulating Bricks is mainly used for clay brick building, blast furnace, hot stove, iron furnace, open hearth furnace and electric furnace and other low temperature part of the use of fireclay refractories. Bricks, bricks for casting systems, heating furnaces, heat treatment furnaces, combustion chambers, flues and chimneys. Clay bricks are especially suitable for large temperature changes.

http://www.yilongrefractory.com/ProductServletOne?id1=1&id=14

2016年11月4日星期五

Basic information on fire - resistant aluminum silicate cotton for industrial furnaces

First, the industrial furnace fire-resistant high insulating brick with fire-resistant cotton is the corresponding fire-resistant material 20mm thick needle-punched blankets made by finishing, size neat, in full compliance with national standards, strict control of the plastic tube in the middle, acupuncture blanket thickness Uniform, all for the fine acupuncture blanket, unlike some enterprises in the middle of the module doping dross blankets, blankets, acupuncture blanket alumina brick slag ball content is low, low degree of hand, used to do all the pre-acupuncture blanket blanket, And there are loading tools to ensure the arrival of the module when the flatness of the company can also provide module installation CD-ROM and supporting the installation of the module tools can cash delivery, I feel dissatisfied may not. Jinan Shengyang fire-resistant ladle slide gate cotton has a good effect of fire-resistant insulation and insulation to improve the overall fire-resistant insulation kiln, and promote the progress of the furnace masonry technology. Classification temperature 1050-1400 ℃.
Note: a variety of fire-resistant cotton, is the corresponding material acupuncture blanket, according to the fiber component structure, size, made in the special machinery. In the processing process, are to maintain a certain percentage of compression to ensure that fire-resistant cotton lining lining is completed, the fire-resistant cotton in different directions of expansion, so that between the fire-resistant cotton into a seamless seamless with each other, Various forms of anchors clay insulating bricks are directly attached to the steel plate anchor bolts of the industrial furnace shell.
Second, the product features: excellent chemical stability; excellent thermal stability; excellent flexibility, the module in the pre-pressure state, in the lining after the completion of the expansion of the module so that the lining seamless and can compensate for fiber lining shrink, Improve the thermal insulation properties of fiber lining, the overall performance is good; excellent thermal stability and thermal shock resistance; ceramic fiber module installed quickly, and anchors set in the cold wall lining, can reduce the anchor material requirements. According to the customer for different furnace insulation design and construction training.
Third, the industrial furnace fire-resistant cotton insulation advantages:
1, cost-effective, construction costs flat or even lower than the brick structure.
2, long life, material composition is extremely stable, stable service life can reach 5 - 10 years, effectively saving maintenance costs and enhance the use of the cycle.
3, energy-saving effect is obvious, a conventional tunnel kiln, a year can save 100-200 tons of coal, reduce costs, increase profits and competitiveness.
4, low density: light insulation than brick lining more than 75% lighter than light weight castable lining 90% to 95%. Such as the use of fiber lining can greatly reduce the furnace load of steel, to extend the furnace life.
5, anti-quench cold hot, will not be damaged due to open shutdown.
6, the construction is simple: the construction process without leaving the expansion joints, construction workers after basic training can be posts, construction technology on the insulation effect of the lining of small.
7, no oven: lining construction can be put into use, no oven program.

Henan Xinmi Changxing Refractory Material Co., Ltd. Located in Henan Province,China.ChangXing's product portfolio covers shaped products such as refractory materials,refractory brick, refractory castable,firebrick refractory,refractory nozzle, ceramic fiber, slide gate, etc; unshaped products including repair, construction and casting mixes and mortars.exported to more than 20 countries, such as Thailand, Indonesia, Pakistan, Saudi Arabia, South Africa, Turkey, Iran, Iraq and so on.

Development and Prospect of Refractories

refractory material is a refractory degree of not less than 1580 degrees, a better thermal shock and chemical erosion, low thermal conductivity and low expansion coefficient of inorganic non-metallic materials. Its widely used in iron and steel, glass, cement and other industries. Refractories have their own characteristics have been proven advantages, but its shortcomings and deficiencies are also different. The development of refractories on the whole in the new products, new processes, such as the direction of development trends.

Refractory material firebrick refractory is mainly made of raw materials such as bauxite, dolomite, silica, magnesite, steel fiber and so on. The development of refractories in the national industrial production applications have a pivotal position.
Refractory materials basic refractories according to the product shape and compact degree, a casting method, melt blowing method, sintering method. Sintering method is part of the raw material pre-firing clinker, cracking and screening, and then a certain percentage of mixing with the raw materials, through molding, drying and firing. The purpose of raw materials is to burn the moisture, organic debris and gas burned. Reduce the sintering products shrink to ensure the accuracy of finished size. In order to homogenize the ingredients and particles of the various raw materials and clinker, kneading is carried out while the binder is added to enhance the bonding strength.

Casting method is to mix raw materials through the process of mixing and fine grinding, in high temperature baking, direct casting, cooling crystallization, annealing into products.

The melt blow method is a method in which the ingredients are melted and then sprayed with high pressure air or superheated steam to disperse them into steel fibers or hollow spheres.

refractory company Henan Xinmi Changxing Refractory Material Co., Ltd. Located in Henan Province,China.ChangXing's product portfolio covers shaped products such as refractory materials,refractory brick, refractory castable,refractory nozzle, ceramic fiber, slide gate, etc; unshaped products including repair, construction and casting mixes and mortars.exported to more than 20 countries, such as Thailand, Indonesia, Pakistan, Saudi Arabia, South Africa, Turkey, Iran, Iraq and so on.

2016年11月3日星期四

Refractory ceramic fiber blanket professional thermal insulation material basic information

Refractory ceramic fiber blanket

Applications: Various industrial furnaces furnace furnace box-type furnace resistance furnace heat treatment furnace quenching furnace annealing furnace back to the furnace vacuum furnace firebrick refractory sintering furnace incinerator carburizing furnace special fire-resistant blanket ceramic fiber blanket, modular products; large-scale furnace equipment dedicated fire Good thermal stability; excellent tensile strength; low thermal conductivity; low heat capacity; excellent sound-absorbing basic refractories noise reduction performance. Features: excellent chemical stability; excellent thermal stability; High-temperature gasket; inorganic fire shutter doors fire-resistant layer; modules, folding block of raw materials. Insulation of high-temperature pipe insulation; electrical components fire insulation; Aerospace special fire - resistant blanket ceramic fiber blanket, module products.

The benefits of ceramic fiber blanket:
◎ In the module on the back of the various forms of the anchor makes the installation of the module can be used side by side arrangement can also be arranged parquet floor arrangement
◎ folding blanket in the lifting of the banding will be squeezed in different directions on each other, do not produce cracks
◎ elastic fiber blanket can resist mechanical external force
◎ ceramic fiber blanket elasticity can compensate for the deformation of the shell, making the gap between the components will not produce
◎ light weight, low heat absorption.
◎ low thermal conductivity can bring high energy efficiency
◎ has the ability to resist any thermal shock
◎ lining without drying and maintenance, so after installation can be put into use immediately
The anchoring system is located away from the hot surface of the assembly, making the metal anchor at a relatively low temperature, improving the safety of the anchorage

refractory company Henan Xinmi Changxing Refractory Material Co., Ltd. Located in Henan Province,China.ChangXing's product portfolio covers shaped products such as refractory materials,refractory brick, refractory castable,refractory nozzle, ceramic fiber, slide gate, etc; unshaped products including repair, construction and casting mixes and mortars.exported to more than 20 countries, such as Thailand, Indonesia, Pakistan, Saudi Arabia, South Africa, Turkey, Iran, Iraq and so on.

2016年11月2日星期三

Refractory concrete of bauxite cement - Basic information

Refractory alumina bauxite concrete is the use of cement, refractory aggregate, admixture and water by a certain percentage of mixed molding, curing and hardening. Bauxite refractory concrete refractory brick with the same high temperature performance of the highest refractory temperature of 1650 degrees, when there are unparalleled advantages of refractory bricks. The refractory bricks in practical application of the formation of arbitrarily poor, and alumina refractory castable can be based on actual needs, according to design requirements, so that the internal structure of the drying furnace to form the ideal surface structure to form the ideal hot air. Thereby increasing the heat utilization rate. Shaped part of the refractory alumina brick masonry in the high temperature state of the overall strength is poor, resulting in residual shrinkage under high temperature, the roof is easy to collapse. The alumina refractory concrete structure is to make up for this shortcoming, it makes the furnace top as a whole structure, strength is very big, will not appear collapse phenomenon. Thereby prolonging the service life of the drying furnace.

The use of alumina castable materials concrete structure, greatly reducing the manufacturing cost. The use of alumina refractory concrete structure manufacturing and repair work is simple, convenient, easy to operate, repair time is short. In short, bauxite refractory concrete and refractory bricks compared to simplify the production process, reducing production costs and improve the quality of the drying furnace, is a better economic refractories.

High strength abrasion - resistant castables for boiler furnaces lining

High-strength refractory castable high strength wear-resistant castable by the high-strength aggregate, powder mineral additive composition, the optimal formulation design, with the smallest wear resistance, high strength, shape can be arbitrarily controlled, the overall strong, simple construction, Due to the addition of polymer, the base layer of concrete bonding firm. High-strength wear-resistant castable cheap, for the requirements of the construction site is the first choice of wear-resistant materials.

High-strength wear-resistant insulating castable refractory is a cement-based composite single-component dry mortar, from the high-strength cement, mineral admixture, high-strength aggregate and anti-cracking agent, the industrial production from the preparation. High-strength wearable castable can be used at the site of mixing with water, good construction workability, by artificial plaster in the silo or high insulating brick mine surface to form a certain thickness of the anti-wear layer, after the normal conservation to achieve technical requirements, with wear resistance High, and the basic concrete (steel silo) bonding strength, impact resistance, high compressive strength, durability, long life and so on. High-strength wear-resistant refractory material castable dedicated to metallurgy, coal, thermal power, chemical, cement and other industries Chong slag ditch, mine trough, unloading trough, the hopper, silo lining material anti-wear layer and water conservancy and hydropower, port and other projects Of the discharge gate, discharge hopper anti-wear layer, play a protective foundation of concrete (or steel silo) role. basic refractories Boiler kiln lining easy to wear parts with high-strength wear-resistant castable HF series castable is widely used throughout the country to build furnace kiln boiler construction and repair works.

Slide Gate Mechanism---Changxing Refractory material

Slide Gate Mechanism---Changxing Refractory material
Slide Gate Mechanism---Changxing Refractory material
Slide Gate Mechanism

Introduction:

Ladle slide gate mechanism, also called ladle slide gate system, slide gate assembly, sliding gate machenism. Ladle slide gate mechanism uses nodular cast iron as raw material. The sealing height is only 110mm. The fan-shaped slide gate plate is equipped with two slide plate blocks. The moving fan-shaped case handle can make one of the slide plate cast hole in working, and make another one moving to the other space of the equipment. At the same time, the moving out slide block can be changed.

Advantages:

1. Slip sheet is force uniform have good stability.
2. Sliding gate lateral clearance self-regulating sensitivity is high.
3. Increase the slip sheet's freedom, bottom slide can vertical-tuning.
4. Have double-sided tight pin; the gab of hinge lateral can be adjusted.

Application:

The slide blocks thicknesses are heightened by this equipment which can be used as rapid nozzle-change mechanism. While add immerse nozzle at the bottom of slide block, the ladle stopper can be replaced and protect the casting.

Content source:
http://www.yilongrefractory.com/ProductServletOne?id1=4&id=54
E-mail:sales8@chinaelong.com

2016年11月1日星期二

Currently the most commonly used method of producing refractory balls

Machine pressure forming method is currently the most used in the production of refractories ball forming method. The method uses a pressure ball machine and a steel mold to press the prepared refractory material into a sphere. Because of the general machine pressure forming refers to the water content of 4% to 9% of the semi-dry material forming method, which is also called semi-dry forming. The method commonly used equipment friction brick press, lever press and hydraulic press and so on.
Machine pressure forming process is essentially a ball material within the particle-intensive and air discharge, the formation of dense sphere process. The ball-forming fire-resistant ball has the advantages of high density, high strength, small drying shrinkage and small shrinkage, easy control of fire-resistant ball size, so this method is the main part in refractory firebrick ball production. In order to obtain a dense sphere during press forming, sufficient pressure must be applied to the pellet. The size of the pressure should be able to overcome the internal friction between the pellet material, to overcome the external friction between the pellet and the mold wall to overcome the insulating castable moisture, particles and fill in the mold caused by uneven pressure distribution Uniformity.
The ratio between the three depends on the ball material dispersion, particle composition, ball material moisture, the size and shape of the sphere. Although the relationship between pressure and the densification of the sphere can be calculated by a number of theoretical formulas, such as the variation of the porosity of the sphere with pressure in logarithmic relation, the experimental method is usually used to determine the pressure per unit area of the sphere, Brick machine should have the total pressure.
Mechanical forming of the ball material requirements in addition to water should have a certain range of fluctuation, its particle size also has certain requirements, such as should have a reasonable grain size ratio, bulk density as large as possible. General critical particle size of 3 ~ 5mm, less than 0.088mm of fine powder content should be 35% to 45% range. The most common defects in machine-formed fire-resistant spheres are the crack and layer density. Spallation is the formation of pressure in the vertical direction of the pressurized layer of cracks. Ball material moisture is too high, too much powder, too little bonding agent and pressure will lead to the production of spall.
Therefore, in the production of these parameters must be controlled. Layer density phenomenon that the shape of the fireball after the density along the pressure direction of the inverter. By the above one-way pressurized insulating refractory cement ball is generally dense under the sparse, the same level is dense in the outer sparse. This is due to the friction between the pellet material and the ball material and the friction between the mold wall caused by the pressure decrease. Double-sided pressure and the wall in the mold coated with lubricating oil to reduce the external friction of the method can reduce this phenomenon and reduce the porosity of the sphere.
Selection of molding equipment should be based on the quality requirements of refractory balls, size and production volume for comprehensive consideration. General refractory ball with a simple fireball or shape, quantity, quality requirements of the general products, the choice of production efficiency of the high pressure ball machine; high quality requirements of the fireball can be nominal pressure not less than 2000K N friction Pressure ball machine.

Henan Xinmi Changxing Refractory Material Co., Ltd. Located in Henan Province,China.ChangXing's product portfolio covers shaped products such as refractory materials,refractory brick, refractory castable,refractory nozzle, ceramic fiber, slide gate, etc; unshaped products including repair, construction and casting mixes and mortars.exported to more than 20 countries, such as Thailand, Indonesia, Pakistan, Saudi Arabia, South Africa, Turkey, Iran, Iraq and so on.

2016年10月28日星期五

Slide Gate Plate---refractory material

Slide Gate Plate

Introduction

Changxing Refractory manufacture various types of slide gate plate, such as 1qc slide gate plate, 2qc slide gate plate. Changxing Refractory slide gate plate uses sintered alumina and mullite as raw material, then be added into some of the carbon matrix components and anti-oxidant(such as aluminum, silicon metal, SiC, B4C, Mg-B and so on), adding binder pitch or phenolic resin mixed with coal Nerishige type, fired in a reducing atmosphere to form alumina oxide carbon refractories sliding gate plate. Slide gate plates fired at high temperatures cover Al2O3-C based, Al2O3-ZrO2-C based and MgO-spinel based, Changxing Refractory supports the customer in flow control offering a range of ladle slide gate products. We have a wide range of refractory materials for achieving consistent and reliable high performance in all areas of slide gate applications. Balanced refractory life of plates, ladle nozzles and well blocks enables a cost-effective operation. Slide gate plate can be used for ladle and tundish.
Advantages

1. High strength
2. Good erosion resistance
3. Excellent thermal shock resistance
Application

The slide gate plate is the best choice for large and medium sized ladles and con-casting tundish. It can meet various needs of different steel grades.


Contect source:
http://www.yilongrefractory.com/ProductServletOne?id1=4&id=53

2016年10月25日星期二

Aluminum Carbon Long Nozzle (Ladle Shroud)

Aluminum Carbon Long Nozzle (Ladle Shroud)

Aluminum Carbon Long Nozzle (Ladle Shroud)

Aluminum Carbon Long Nozzle (Ladle Shroud)

Introduction

Based on function categories, Changxing Refractory aluminium carbon long nozzles(also called Ladle Shroud, Long Nozzle) can be classified into preheating refractory nozzle, non-preheating refractory nozzle, argon blowing nozzle and not argon blowing nozzle; and according to material quality, ladle shroud are mainly classified into aluminum carbon, aluminum-zirconia carbon and alumina-magnesia carbon. This kind of refractory nozzle is provided with good liquid steel washing resistance performance and liquid steel erosion performance in the course of use, which can effectively prevent oxidation of air to liquid steel and its spatter.


Advantages and Application

Changxing Refractory ladle shroud enjoys performances of purifying liquid steel, prevent liquid steel oxidation, with good liquid steel washing resistance and erosion resistance.

Content source:
http://www.yilongrefractory.com/ProductServletOne?id1=3&id=50

2016年10月24日星期一

High Temperature Refractory for Furnace - Ceramic Fiber Paper

product manual:

With ceramic fiber as the main raw material, made by wet forming process, with high temperature resistance, chemical corrosion, thermal shock, low thermal conductivity, high electrical Insulating Bricks strength and high elastic modulus and other properties. It is characterized by no asbestos, fiber length, less slag balls, small bulk density, good elasticity, Easy to punching, winding and other construction operations. It is suitable for high temperature insulation, heat insulation, sealing, electric insulation, sound absorption and filtering fiber distribution, color white, no delamination, less slag ball (four centrifugal slag), bulk density according to the use of flexible adjustment, increase Strong fiber), mechanical processing and strong, can replace asbestos products, is a high-grade lightweight refractories. Non-brittle material, good toughness, high compressive strength, good flatness, size regularity, excellent mechanical properties and easy construction of any shear bending. Is the kiln And other thermal equipment wall lining, the ideal backing material.

Ceramic Fiber Paper Application:

Industrial kiln wall lining, masonry insulation layer High temperature ceramic kiln kiln lining, kiln car, furnace door baffle, kiln furnace temperature partition board high temperature high heat equipment thermal insulation Aerospace, shipbuilding industry insulation, fire protection, Insulation, insulation - Technical features: low thermal conductivity, low heat capacity, excellent Thermal stability and thermal shock resistance high compressive strength, and has good toughness!

⊙ Typical Applications:

● a variety of industrial furnaces and ladle, casting barrels, immersion nozzle of the high-temperature insulation materials;
● electric insulation and insulation materials for industrial furnaces;
● door and furnace expansion joint sealing material;
● cast aluminum model lining;
● stripping of glass-ceramic and hot-melt (curved) glass;
● high temperature gasket materials;
● muffler insulation muffler materials, exhaust pipe insulation materials, anti-sintering isolation materials.

Refractory company Henan Xinmi Changxing Refractory Material Co., Ltd. Located in Henan Province,China.ChangXing's product portfolio covers shaped products such as refractory materials,refractory brick, refractory castable,refractory nozzle, ceramic fiber, slide gate, etc; unshaped products including repair, construction and casting mixes and mortars.exported to more than 20 countries, such as Thailand, Indonesia, Pakistan, Saudi Arabia, South Africa, Turkey, Iran, Iraq and so on.

High temperature refractory insulation material for kiln - ceramic fiber cotton

Product manual:

The basic characteristics of the ceramic fiber loose cotton are the stable performance, light weight, low heat capacity, good thermal shock resistance, erosion resistance and sound absorption performance under the high temperature condition. Modern high-tech light-resistant materials can make suitable for special requirements, full Foot customer needs. Ceramic fiber cotton Silicate fiber cotton with stable performance, fiber length, tensile strength, large slag ball, high thermal stability, color,white and so on. Classification temperature 1050-1600 ℃. Is the production of fiber textile materials of choice, but also high temperature environment Sealing, filling and insulation of the ideal refractory material.

Product Features:

Low thermal conductivity, thermal shock resistance, high flexibility, good sound-absorbing properties, without any binder and other corrosive substances, high temperature is still loose and flexible and has good flexibility Anti-corrosion, excellent sound absorption, excellent Thermal stability.

Typical application:

Industrial ceramic fiber wet raw materials; ceramic fiber unshaped products of raw materials; high-temperature furnace, heating device, wall lining gap filler and so on.

First, as the base material, can be used as plate, paper, vacuum forming parts and other fiber deep processing of raw materials

Second, the expansion joints or short-term insulation repair filler material

Third, thermal insulation concrete and composite reinforcement

Four; high-temperature furnace, heating devices, wall lining gap filler with ceramic fiber cotton
Note: Because of its high performance characteristics, will be a revolutionary solution to a variety of technical problems, its application areas for metallurgy, ceramics, electronics, building materials, automotive, aerospace, glass and so on.

Refractory company Henan Xinmi Changxing Refractory Material Co., Ltd. Located in Henan Province,China.ChangXing's product portfolio covers shaped products such as refractory materials,refractory brick for sale, refractory castable,refractory nozzle, ceramic fiber, slide gate, etc; unshaped products including repair, construction and casting mixes and mortars.exported to more than 20 countries, such as Thailand, Indonesia, Pakistan, Saudi Arabia, South Africa, Turkey, Iran, Iraq and so on.

Selection Principle and General Method of Refractory for Furnace

The main performance of the furnace is mainly determined by the technical and economic performance of the refractory insulation material, which directly affects the investment cost, working performance, thermal efficiency and running energy consumption of the kiln. Select the general principles of fire-resistant insulation materials:
1, the performance of the kiln and thermal characteristics, such as the gap between the work of the kiln should use low heat capacity of the material;
2, the safe use of materials temperature, thermal conductivity system, high temperature strength, chemical stability;
3, the use of life;
4, investment costs and operating maintenance costs.

In general, heavy refractory material is more focused on a technical performance indicators, such as high temperature stability, chemical stability; light weight insulation materials pay more attention to investment and operation of the integrated technical and economic indicators.

When using lightweight insulation materials, the general thermal insulation material thermal conductivity (λ) and the cost per unit volume of insulation material (P) to determine, "λP" product value as small as possible. Thermal conductivity value is small, indicating the insulation effect of insulation materials, running the energy costs low. Low cost per unit volume of insulation material that investment costs are low, with good investment in economic results. Can be plotted with coordinate mapping choice, the abscissa for the operating temperature, the vertical coordinate (λP) good product, with the safe use of materials, intercept the temperature curve of the material, Select the technical and economic performance of the material.

Refractory company Henan Xinmi Changxing Refractory Material Co., Ltd. Located in Henan Province,China.ChangXing's product portfolio covers shaped products such as refractory materials,refractory brick, refractory castable,refractory nozzle, ceramic fiber, slide gate, etc; unshaped products including repair, construction and casting mixes and mortars.exported to more than 20 countries, such as Thailand, Indonesia, Pakistan, Saudi Arabia, South Africa, Turkey, Iran, Iraq and so on.

2016年10月19日星期三

How to Choose Refractory Brick Molding Equipment

Refractory plant Refractory company plant new shape, you must buy the press. If such enterprises for small and medium-sized manufacturing plant, according to the current and future production of products may choose the right tonnage friction press. Because of the low price of friction press, operation and maintenance is simple, more suitable for small and medium enterprises.
Expansion or technological transformation of enterprises, according to need to purchase some brick press. For large and medium-sized refractory material production enterprises, if you need to produce high-grade products or high-performance products, according to the specific product selection of suitable molding equipment. Such as the production of functional refractories dry vibration mix and other special products, such as optional hydrostatic forming device; such as the production of high-grade lining brick, can choose more advanced hydraulic press machine or a vacuum function of the press, can also use large tonnage Friction press brick.
Older machine update is relatively simple, according to the original models and have advanced to buy the more advanced press or other molding equipment.
The purchase of molding equipment and purchase other equipment, is to consider a number of factors to decide, and not ladle gunning mix above the situation can be summarized. For small and medium enterprises, the production plant can refer to other molding equipment to choose, in addition, the purchase of molding equipment, technical parameters should be surplus, there should be a certain sense of advance to meet the continuous development of technology and production needs.
Henan Xinmi Changxing Refractory Material Co., Ltd. Located in Henan Province,China.ChangXing's product portfolio covers shaped products such as refractory materials,refractory brick, tundish coatingrefractory castable,refractory nozzle, ceramic fiber, slide gate, etc; unshaped products including repair, construction and casting mixes and mortars.exported to more than 20 countries, such as Thailand, Indonesia, Pakistan, Saudi Arabia, South Africa, Turkey, Iran, Iraq and so on.

Development Prospect of Refractories in China

In recent years, the level of China's refractory material industry has also been increasing, but the general demand for refractories will be substantially reduced, and high-quality, long life, high efficiency, functional refractories and the corresponding increase in demand, refractory dry vibration mix enterprises need to continuously improve the comprehensive Strength, in particular, to improve research and innovation capacity, and constantly develop high-life refractory products to meet the needs of users. In order to achieve the high life of refractories, in addition to improving the performance of refractory itself, the application of refractory technology is also very important to increase the comprehensive application of refractory technology research and development of refractory high life to meet the high-temperature steel and other industries to reduce fire Material consumption needs.

The future of refractory tundish castable technology will be longevity, low consumption, energy saving, environmental protection, low carbon, recycling and functional integration of the direction of research and innovation, thereby enhancing the comprehensive service capabilities, from the overall upgrading of China's international competitiveness of refractory industry , Refractory industry will also lead the development of China's special materials industry, technological revolution and rapid development.

(A) the development of energy-saving environment-friendly refractory industry

Refractory material is an important auxiliary material in the steel industry, and has wide application in the national steel industry. At present, China's annual consumption of refractories is about 10 million t, with the use of waste refractories to 400 million t, the proportion of refractory refractory refractory consumption of 45% of the total. If the recycling of refractory materials can be recycled high-grade raw materials, the use of renewable raw materials and optimize their bonding agent and additives, not only can produce high-quality unshaped refractories, but also produce high-quality shaped refractory, but also large Reducing the cost of preparation of refractories; not only saves the country's mineral resources and energy, but also reduces environmental pollution, can effectively reduce product costs and promote the overall development of the steel industry, economic and social benefits significantly.

Therefore, the refractory enterprises need to further improve the production level of all-round, and gradually the full use of clean, low-carbon environment-friendly energy, increase efforts to improve the recycling of waste refractory, waste refractory comprehensive utilization technology, Waste heat utilization technology, vigorously develop the circular economy, as far as possible to reduce the production process of waste emissions, to avoid the production of waste on the environment pollution. In addition, enterprises should speed up the elimination of production capacity inefficient production equipment, increasing the share of unshaped refractories, vigorously develop low-temperature sintering or burning and other new technologies, fundamentally improve the ability of sustainable development of refractories.

(B) the development of internationally competitive refractory industry

Competitiveness has always been the problem of all walks of life has always attached importance to, but also the fundamental survival of enterprises. The future development of China's refractory industry, will focus on the international, seeking to achieve greater development in the world and profitability. In recent years, with the continuous development of refractory industry, China's refractory production level is close to or reached the international advanced level, product cost, quality are strong international market competitiveness. Products not only by Southeast Asia, the Middle East and other developing countries of all ages, but also a large number of exports to Europe and the United States and other developed countries, and achieved good results, which also shows that China's refractories enterprises are not satisfied with the domestic marketing, Has been very far-sighted in this larger stage in the world to obtain greater profits, and also proved that China's refractory products have the strength and ability to achieve significant international development.

(C) the development of comprehensive technical level of refractory industry

Refractory material industry with comprehensive technical level not only refers to producing refractory products with good quality, environmental protection, light quality and other high-quality features, but also refers to the production of refractory matching equipment with long life, good performance, high yield and other high-quality features. Comprehensive technical level of assessment factors, involving refractory products and production equipment, such as a set of process, as well as a high level of product development, supervision and management personnel and other factors, the comprehensive evaluation of these factors determine the refractory industry comprehensive technical level.

In addition, the overall contracting refractory enterprises must also have a certain iron and steel enterprises to have a certain refractory product development and quality improvement of the autonomy, according to the steel enterprises in different parts of high temperature equipment, the erosion of refractory differences, relying on enterprise technology Different parts of the refractory materials used to optimize the configuration, give full play to the potential use of refractories, refractories to improve service life and reduce steel consumption of refractories. Because of its unique advantages and strong adaptability, the refractory material whole contracting mode will become an advanced mainstream business model which is unanimously recognized and widely applied by the steel industry and all high temperature industries.

Therefore, enterprises engaged in the overall contracting of refractories must change from the original manufacturer to the comprehensive service provider, and promote enterprises to pay more attention to science and technology investment, enhance innovation ability, strengthen production equipment, strict production, masonry construction and other links Quality, so that the comprehensive technical ability of enterprises to continuously upgrade and further enhance the competitiveness.

Refractory company Henan Xinmi Changxing Refractory Material Co., Ltd. Located in Henan Province,China.ChangXing's product portfolio covers shaped products such as refractory materials,refractory brick for sale, refractory castable,refractory nozzle, ceramic fiber, slide gate, etc; unshaped products including repair, construction and casting mixes and mortars.exported to more than 20 countries, such as Thailand, Indonesia, Pakistan, Saudi Arabia, South Africa, Turkey, Iran, Iraq and so on.